Fibre fineness — where it appears

The linear density of a single fibre, in decitex, which fixes its diameter once a density is known. It decides how many fibres are in a yarn's section, and therefore both the width of this site's bending bracket and how hard a fold strains the fibres in it.

Named by 16 essays across 6 fields — each of them below, with the objects they name alongside it.

The evenness a cotton yarn cannot be better than. Lay staple fibres down at random and count how many cross a plane: the count is Poisson, its variance is its mean, and the coefficient of variation of the mass per unit length is therefore 1/√n with no material and no machine in it. The lower curve is that floor. At 20 tex there are 118 fibres in the section and the floor is 9.93 per cent; at 5 tex there are 29 and it is 19.86. The upper curve is what a yarn spun at an index of irregularity of 1.35 actually measures, which is the floor times a constant — so the whole shape belongs to the counting and none of it to the spinning. The exponent is exactly −½ and is asserted as such rather than fitted to the curve.

The spread was never free

This collection has taken a yarn's irregularity off a delivery note and used it as an input. It is not an input. Counting the fibres in a cross-section puts a floor under it that no spinner can beat, and the floor is one over the square root of the count.

cloth · Variation A 5.0 mm cotton pile standing and crushed. A pile tuft standing 5.0 mm proud and the same tuft pressed flat, which turns it through a right angle over its own length and so bends it to a radius of 3.18 mm. Its fibres are strained 0.187% — an order of magnitude below the smallest strain anybody has measured a recovery at, so this file declines to say what fraction comes back. The consequence is that a crushed carpet is not held down by its fibres: what keeps a pile flat is the tufts leaning on one another and the friction where they touch. Below 0.469 mm the fibre does enter its measured range, which is the difference between a carpet and a velvet and has nothing to do with what either is made of. What the drawing cannot show is the neighbouring tufts, which are the mechanism.

A crushed pile is not held down by its fibres

A carpet flattened under a foot has bent its tufts through a right angle, which sounds severe and is not: the fibres in a five-millimetre pile are strained under two tenths of a per cent, an order of magnitude below the smallest strain anybody has measured a recovery at. What holds a pile down is the tufts leaning on one another.

fancy · Pile The tightest fold a 20 tex cotton yarn can be given. A cloth folded as sharply as it can be folded. The two yarn crowns on the inside of the fold cannot pass through one another, so the fold's radius is the yarn's own — 0.084 mm for a 20 tex cotton yarn — and there is no measurement of an iron anywhere in the argument. At that radius a fibre free to slide is strained 7.14%, which is √(packing × fibre tex ÷ yarn tex), and the whole yarn bending as a rod would be strained exactly one hundred per cent. Cotton's measured breaking extension is 6.0% to 10.0%, so the free bound does not survive and the locked one cannot. What the drawing cannot show is the fibres inside the yarn, which is exactly what the argument is about — the picture is the same either way and the strain is fourteen times different.

A crease is a fold the crimp cannot supply

A fold needs its outer face longer than its inner, and a woven cloth's way of supplying a length is to move crimp. That runs out at a radius of millimetres, and a pressed crease is tenths of one — so the fold is handed to the fibres. How hard it strains them turns on a question this collection has been unable to settle for two fields, and a crease settles it by refusing.

finishing · Crease Elastic recovery against strain, for seven fibres. The elastic recovery of seven fibres at the strains it is reported at: extend to a stated strain, unload, read the strain returned immediately. Each fibre's points are joined and the line stops where the measurements stop, which is the point of the figure — a fibre strained past the last point on its own line is a fibre this collection declines to answer for. Nothing here is measured below one per cent of strain, and a woven cloth just past its own interchange budget is at a thread strain of a few hundredths, so the region that matters most for a fabric is the region nobody has reported. Recovery falls monotonically for every fibre, which is what lets the unmeasured region be bracketed between the lowest measured value and one rather than extrapolated. What the plot cannot show is the delayed recovery, which is excluded by the convention and is largest for the fibre with the best reputation for recovering.

Recovery is measured and nothing predicts it

A fibre's stiffness is a bracket this collection can compute the ends of. What fraction of a strain it gives back is not: it has to be looked up, the tables are thin, they stop exactly where a fabric needs them, and the most attractive explanation for the ordering they show turns out to have no signal in it at all.

mechanics · Yarn stiffness The strain at a fold against the strain each fibre breaks at. For each fibre, the surface strain at the sharpest fold a 20 tex yarn of it can make — which is √(packing × fibre tex ÷ yarn tex), with no measurement of a crease in it — beside its own measured breaking extension. cotton and flax are strained past the low end of their breaking range, so some of their fibres break at the fold, and that is what a linen crease is. The rest survive, and among them viscose and wool return less than three fifths of what they were given, which is the other way a cloth creases. Both columns are needed: viscose survives with a factor of two to spare and is among the three worst by measurement. What the bars cannot show is wool, which the census puts in the wrong column because the recovery figures are the immediate ones and wool's is the most delayed of any fibre here.

Which fibres crease, and why there are two answers

Run the sharpest fold a yarn can make against every fibre's breaking extension and its recovery, and the ranking that falls out is the trade's own — linen worst, cotton next, wool and the melt-spun filaments best. It falls out of two columns rather than one, because two fibres in the bottom three get there by different mechanisms, and a treatment that fixes one does nothing for the other.

finishing · Crease The two diameters of a 20 tex yarn. The pressure inside a twisted yarn is zero at its surface, so the outermost fibres are held by nothing but their own buried ends and some of them stand off as loops and ends. A yarn therefore has two diameters: a mass diameter of 167.1 µm, which is a volume divided by a length and is the one every other calculation on this site uses, and a contact diameter of 217.1 µm, which is what a neighbouring thread, a finger or an air stream meets. The gap is a hair layer of 25.0 µm on each side and it is measured, not computed — nothing here predicts hairiness. What is computed is the consequence, and it is 29.9% of the diameter every cover factor on this site was built from.

Singeing is the cheapest change to a surface

Pass a cloth through a flame fast enough and it loses under one per cent of its mass. What it loses is the part of itself that was doing most of the touching, and lustre, friction, printability, pilling and measured cover all move at once.

finishing · Hairiness 20 tex, counted. The cross-section of a 20 tex cotton yarn, with every fibre in it drawn. The count is a division and nothing else: a 20 tex yarn spun from 0.17 tex fibre has 117.6 fibres crossing any plane through it, and the yarn is 14.0 fibre diameters across because n fibres packed at 0.6 fill a circle √(n/φ) times as wide. The arrangement is drawn on a lattice and is not claimed: real fibres are not on one, they migrate between the core and the surface as they run, and everything this collection says about a yarn's strength turns on their doing so.

How many fibres make a thread

Every number in this collection began with a diameter, and a diameter is not a measurement — it is a count of fibres, divided. Once the division is written down, three quantities that had nothing to do with each other turn out to be the same number.

setting · Assembly One hairiness reading does not fix the other. Every yarn on this curve has exactly the same total protruding fibre length — the quantity an integrating hairiness meter reports — and they differ in how that length is distributed. The count of hairs at least three millimetres long runs from 170 to 4354 per hundred metres, a factor of 26, across decay lengths real yarns actually have. The two instruments read two functionals of one population: the first moment N₀λ and the tail N₀e^(−3/λ). A correlation between them can exist only if λ is fixed across the yarns being compared, and λ is a fibre property, so it is not. That is the whole of why the trade's two hairiness numbers have never agreed, and it is arithmetic rather than instrumentation. What the figure cannot show is which of the two predicts anything: the tail does, because pilling, prickle and a printed edge all need reach.

Two hairiness meters read two moments

The trade has two instruments for yarn hairiness and thirty years of failing to predict either from the other. They are not measuring the same thing badly. One reports the first moment of a distribution and the other reports a tail probability, and two functionals of one curve are related only through a parameter neither of them reports.

cloth · Hair layer The pressure a 23° twist puts on its own fibres. A twisted yarn squeezes itself. Every fibre under tension at a radius pulls inward with sin²θ of its tension per unit length, and integrating outward to the surface — where the pressure is zero by definition, because there is nothing outside to push against — gives p(r) = ½σ(cos²θ(r) − cos²α) in closed form. At a surface angle of 23° the pressure on the axis is 7.6 per cent of the core fibre's own axial stress and the mean over the section is 3.61 per cent of it. The shading is that closed form and the curve is the same function plotted; the shape is what matters, and its one uncompromising feature is the zero at the edge. The outermost fibres are held by nothing, which is why a yarn is hairy, why a surface fibre is the one that comes away on a finger, and why singeing changes a yarn's behaviour out of all proportion to the mass it removes.

What grips the end of a fibre

A twisted yarn squeezes itself, and the squeeze holds the fibre ends in. Write the slip and the break out side by side and the fibre's own strength cancels — and so does the load on the yarn — leaving a gripped length that depends on fineness, friction and the twist and on nothing else.

mechanics · Migration Thirty micrometres is a buckling load. The wool fibre diameter at which a protruding end reaches the measured threshold for prickle, against how far it protrudes. A fibre end pressed against skin is a column held at the cloth and free to slide at its tip, so it buckles at 20.19EI/ℓ² and carries no more load than that; below the threshold it bends away and is felt as touch, above it the load stands and is felt as pain. At a two-millimetre protrusion — which this site's own hair model puts in the top fifth of a wool's population — the threshold diameter is 32 µm, bracketed at 29–34 by the range of the measured force. Neither the thirty micrometres nor the two millimetres was put in. The band is the force bracket, and the fourth power in I = πd⁴/64 is what makes the boundary sharp: at a mean of 21 µm and a spread of 24%, 3.2% of the fibres are over it, and it is that few per cent that decides whether a garment can be worn.

Prickle is a buckling load

The wool trade specifies comfort against skin by the percentage of fibres coarser than thirty micrometres, and the thirty is a measured boundary with no derivation attached. It is a column formula: solve for the diameter at which a protruding fibre end stops bending away and starts standing its ground, and thirty micrometres falls out.

applied · Prickle The depth belongs to the fibre and the density to the yarn. Over a 5-fold range of cotton yarn counts, the hair layer's decay length moves by 6.2% and its population moves by 2.37-fold against a square root of 2.24. Both follow from one cancellation. The shell's share of the section is 4d_f/D, the migration period is a fixed number of yarn diameters, and λ = ½(kD)(4d_f/D) — the yarn's diameter divides out and leaves λ = 2k·d_f, a length belonging to the fibre alone. The density has no such cancellation and goes as √(nφ)/L. The two small departures visible here are not two facts: they are the shell's second-order term, and they are the same number to the last bit of a double. The consequence for a spinner is that a coarse yarn is hairier and its hairs are no longer, so everything that depends on reach — pilling, prickle, a printed edge — is decided by the fibre and not by the count.

Hairiness goes as the root of the count

A coarse yarn is hairier than a fine one and everybody knows it. What nobody has said is that its hairs are no longer — the count and the length obey different laws, one rises as a square root and the other does not move at all, and the identity behind both was asserted on this site for an entirely unrelated reason.

setting · Hair layer What a knot costs, and what decides it. Knot efficiency against the radius the thread is bent to, for 5 fibres at 20 tex, computed at the free end of the stiffness bracket — each fibre bending about its own axis, so the strain at the outside of the bend is half a fibre diameter over the radius. At one yarn diameter of radius, cotton keeps 46%, which is the rule of thumb that a knot halves a rope's strength. What separates the curves is not the knot and not the friction: it is the fibre's own breaking strain, which is how much the bend is allowed to spend before there is nothing left.

A knot halves a yarn and says why

The rule is quoted for every rope and every knot and derived nowhere. It comes out at forty-six per cent for a cotton — but only if the yarn's fibres bend individually. A yarn bending as a solid section has already spent five times its breaking strain before any load arrives, so it could not be knotted at all.

applied · Tensile A cotton yarn at a fold, at both ends of its bending bracket. The same 20 tex cotton yarn bent to a radius of 0.084 mm under the two assumptions this site's bending bracket is drawn between. If the fibres slide freely past one another each bends about its own middle and the surface strain is 7.14%; if they are locked the bundle bends as a rod and the outermost fibre is strained 100%. The ratio is 14.0, which is the ratio of the two diameters and therefore the square root of the fibre count over the packing — so the bracket of 327 this site carries in a stiffness is a bracket of 14.0 in a strain. What the drawing cannot show is which of the two a real yarn does, and the answer is settled by a refusal: at the tightest fold a cloth can make, the locked bound asks for a strain of one, and a creased cloth does not fall apart.

A wrinkle cannot settle what a crease settles

The first rung of this ladder found that a pressed crease decides a question this collection had been unable to settle for two fields — whether a bent yarn's fibres slide or bend as one body — and it decides it by refusing: the coherent branch would strain the fibres by eighty-four per cent and cotton breaks at six. A wrinkle is the same fold at twenty times the radius, and there both branches are survivable. So the bracket that a crease collapses stays fourteen times wide at every radius anybody actually creases a cloth at accidentally.

finishing · Crease What a knot costs, and what decides it. Knot efficiency against the radius the thread is bent to, for 5 fibres at 20 tex, computed at the free end of the stiffness bracket — each fibre bending about its own axis, so the strain at the outside of the bend is half a fibre diameter over the radius. At one yarn diameter of radius, cotton keeps 46%, which is the rule of thumb that a knot halves a rope's strength. What separates the curves is not the knot and not the friction: it is the fibre's own breaking strain, which is how much the bend is allowed to spend before there is nothing left.

Which yarns knot well

A knot's efficiency depends on three things and only one of them is the knot. The other two are the fibre's fineness and its breaking strain, and across this collection's own table those give efficiencies from six per cent to eighty-three at exactly the same bend.

applied · Tensile A fibre's two stiffnesses, as the ratio that survives the bracket. C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it.

The one fibre whose answer is known

A table of measured constants is worth what its worst row is worth, and nobody can tell which row that is. This one has a member whose answer was known before anybody measured it, and the ordering of the other nine turns out to say something about how fibres are made.

mechanics · Torsion What the count moves at 150 grams. Plain cotton cloths that all weigh 150 g/m², from 20 tex to 200 tex, with sett and crimp solved together. Thickness, which is two yarn diameters, rises 3.16 times across the line; the cover factor of each thread system falls 2.75 times; their product with one plus the crimp is the same number at every count, because the weight has fixed the volume of fibre and the count only decides whether it is laid out flat or stacked up.

A weight fixes the fibre and not the drape

Every plain cotton cloth of 150 grams a square metre contains the same fibre, and the count decides only how it is arranged. Across the counts that can make that weight, thickness rises threefold and cover falls in step, so their product holds still. The bending length does something stranger: at the bound a woven yarn actually sits near, it depends on neither the count nor the weight, only on the fibre.

setting · Weight

Named alongside it

The objects these essays reach for when they reach for this one.

Packing factorBending rigidityElastic recoveryFibre countSpecificationTenacityYarn diameterBreaking extensionFold radiusMeasurementStaple lengthBending bracket