Stress concentration — where it appears

The rise in stress at the edge of a hole in a continuum, which a woven cloth avoids because each thread carries its own load. A cloth does not have one because each thread is independent, which is why a fabric does not mind a hole and a plate does.

Named by 3 essays across 2 fields — each of them below, with the objects they name alongside it.

A cloth does not mind a hole. Strength left after a hole, against the width of the hole, for a woven cloth and for a film of the same width. The cloth's threads carry their own load, so it loses exactly the threads the hole removes and the loss is linear. The film is a continuum, so a hole of any size at all costs it the stress concentration factor — quoted from Kirsch's elasticity solution, not derived here — and the size of the hole does not enter.

A cloth does not mind a hole

A hole in a film costs it two thirds of its strength whatever the hole's size, because a continuum concentrates stress at an edge. A cloth's threads carry their own load and hand almost nothing to their neighbours, so a hole costs exactly the threads it removes — a loss that is linear in the hole, independent of the sett, and zero for a slit along the load.

applied · Damage What a coating does to the rest of the site. Seven quantities this site computes for uncoated fabric, with what each becomes once a film bonds the crossings: the shear a cloth will take — changed in kind; tear strength — changed in kind; the loss from a hole — reversed; wicking — halved; air permeability — reversed; the sett's effect on strength — unchanged in sign; areal weight — added to. Two of the seven reverse outright. The table is a collection rather than a computation, and each row points at the essay whose result it qualifies.

Coated is a state

Every mechanism on this site assumes threads that can move relative to one another — the bias is a mechanism because the crossings rotate, a tear runs because threads gather, a cloth takes a hole without minding because the neighbours pick the load up. A film bonds the crossings. Two of those results reverse outright, the rest change in kind, and no number on this site has ever said which state it belongs to.

finishing · Coating What a tear asks for is the weakest of a few. A tensile test pulls every thread in the width and averages them. A tear pulls the handful in the triangle at the tip of the cut, and what lets it move is whichever of those is weakest — so the quantity that governs is the minimum of a small sample, and two things follow that no mean can show. Its expectation is below the mean: at CV 15% the weakest of 4 is 0.853 of the mean thread, and the weakest of 40 is 0.718. And its scatter is enormous compared with a tensile test's: 10.9% against the 0.75% a mean of four hundred threads would show. A tear strength that varies by a tenth between specimens of the same cloth is not a badly run test. It is the only answer an extreme of four can give.

A tear asks fewer threads than a pull

A strip test averages a hundred threads and a tear interrogates four. That difference alone accounts for the two things everybody knows about tear testing — that it reads low, and that it scatters — without anything about the cloth being different between the two tests.

applied · Damage

Named alongside it

The objects these essays reach for when they reach for this one.

PropagationAreal weightBiasCoatingCoefficient of variationDirectionFilmFrayingFrictionLadderingMeasurementNet section