Permanent set — where it appears

The part of a deformation that does not come back when the load is taken off. It has two separate causes — fibres strained past what they return, and friction holding the crossings where they were left — and the two respond to different remedies.

Named by 14 essays across 5 fields — each of them below, with the objects they name alongside it.

The two routes a poplin has to a strain. A poplin drawn in section at three places: as woven, at the end of what its crimp can supply, and past that. Between the first two the warp's crimp falls from 8.97% to 4.85% and the weft takes on what it gave up, and the thread length is 0.4953 mm in both — nothing has stretched, and the cloth is 3.93% longer. Between the second and the third the geometry cannot move because the weft's straight run has vanished, so the cloth's extra 2.0% is the thread's extra 2.0%. What the drawing cannot show is which of the two a piece of cloth has had: the first two states look different and the last two look the same, and it is the last two that differ in whether the cloth comes back.

A cloth gives back less than it took

Everything this collection computes about a deforming fabric is reversible, and no fabric is. The repair is not a new material property: a woven cloth has two routes to a strain, one of them costs its threads nothing and comes back in full, and where the first route runs out is a number about the sett with no fibre in it at all.

cloth · Memory A 5.0 mm cotton pile standing and crushed. A pile tuft standing 5.0 mm proud and the same tuft pressed flat, which turns it through a right angle over its own length and so bends it to a radius of 3.18 mm. Its fibres are strained 0.187% — an order of magnitude below the smallest strain anybody has measured a recovery at, so this file declines to say what fraction comes back. The consequence is that a crushed carpet is not held down by its fibres: what keeps a pile flat is the tufts leaning on one another and the friction where they touch. Below 0.469 mm the fibre does enter its measured range, which is the difference between a carpet and a velvet and has nothing to do with what either is made of. What the drawing cannot show is the neighbouring tufts, which are the mechanism.

A crushed pile is not held down by its fibres

A carpet flattened under a foot has bent its tufts through a right angle, which sounds severe and is not: the fibres in a five-millimetre pile are strained under two tenths of a per cent, an order of magnitude below the smallest strain anybody has measured a recovery at. What holds a pile down is the tufts leaning on one another.

fancy · Pile The shear a dome demands, against how far round it the cloth reaches. A flat sheet of inextensible threads takes a double curvature only by shearing, and the shear it needs depends on how far round the dome it has to reach rather than on how big the dome is — a knee, a shoulder and a beach ball demand exactly the same at the same fraction of their own radius. The horizontal line is the locking angle for a sheeting, where the threads are touching side by side and the mechanism has nowhere left to go. Reaching one radius round takes the cloth to 85% of that, and reaching 1.2 radii passes it. What the plot cannot show is the frictional part: a shear well inside the locking angle is still a shear at crossings friction is holding, so a knee that is domed a thousand times keeps a little of each one.

A knee is a dome imposed a thousand times

A flat sheet of inextensible threads takes a double curvature only by shearing, and how much shear it needs depends on how far round the dome it has to reach — not on how big the dome is. So a knee and a beach ball demand the same, and a trouser knee covered to its own equator is at 85 per cent of the angle at which the threads touch side by side.

applied · Damage The poplin's two budgets as it is held stretched. What is left of a poplin's interchange in each direction as it is held at more and more warp strain. The warp's budget falls to nothing at 3.93%, which is the point of the curve; the weft's rises, because the crimp the warp gives up is crimp the weft takes on. There is one locus and one position on it, so the two are not two quantities that happen to be related — they are the two distances from one point to the two ends of one curve. The consequence is that a pre-tensioned cloth has almost no warp recovery left and more weft recovery than it started with. What the plot cannot show is that the exchange rate between them is not constant: the curve is not a straight line, and its slope is the Poisson ratio this site computes elsewhere.

A cloth has one budget for two directions

A woven cloth looks as though it carries two independent reserves of free extension, one along the warp and one across the weft. It carries one. There is a single curve of states and a single position on it, so every hundredth spent one way is refunded the other — which means a pre-tensioned cloth has not used its recovery up, it has moved it.

mechanics · Tensile Wash-by-wash shrinkage, reported and modelled. The shrinkage an unfinished cotton cloth shows in each of five laundering cycles, beside what a model with no rate in it predicts. The model says a wash lets every crossing whose frictional barrier is below the cloth's current excess slip to the edge of its own band, and that is a distribution rather than a rate. Two numbers are fitted — the excess the cloth came off the loom with, 7.13%, and the spread of the barriers, 37.2× — against the first two washes. Washes three, four and five are predictions with nothing left to adjust and come out at 0.506%, 0.284%, 0.179% against reported 0.50%, 0.30%, 0.20%. What the bars cannot show is the finding underneath: the reported yarn-on-yarn friction range gives a spread of only 1.34×, which would have the tail over by the third wash.

A cloth shrinks most the first time

A laundering test reports five numbers and they fall away like a geometric series. Nothing in a wash is slow — a cloth is agitated tens of thousands of times in half an hour — so a second wash that shrinks it again is direct evidence that its frictional barriers are spread, and the ratio between successive washes measures how far.

finishing · Shrinkage Elastic recovery against strain, for seven fibres. The elastic recovery of seven fibres at the strains it is reported at: extend to a stated strain, unload, read the strain returned immediately. Each fibre's points are joined and the line stops where the measurements stop, which is the point of the figure — a fibre strained past the last point on its own line is a fibre this collection declines to answer for. Nothing here is measured below one per cent of strain, and a woven cloth just past its own interchange budget is at a thread strain of a few hundredths, so the region that matters most for a fabric is the region nobody has reported. Recovery falls monotonically for every fibre, which is what lets the unmeasured region be bracketed between the lowest measured value and one rather than extrapolated. What the plot cannot show is the delayed recovery, which is excluded by the convention and is largest for the fibre with the best reputation for recovering.

Recovery is measured and nothing predicts it

A fibre's stiffness is a bracket this collection can compute the ends of. What fraction of a strain it gives back is not: it has to be looked up, the tables are thin, they stop exactly where a fabric needs them, and the most attractive explanation for the ordering they show turns out to have no signal in it at all.

mechanics · Yarn stiffness What a tensioned sheeting has left of its load. A sheeting pulled to a strain, clamped at that length and left. Its length does not change, and its load does: crossings rearrange locally until the load has fallen to what friction alone can hold, which is 0.0756 N per end and is the same number whatever the cloth was pulled to. So the fraction retained is that floor over the load applied, and it falls — a cloth tensioned to 4.94 per cent keeps 29 per cent of what it was given. Below the resting band's own edge nothing is lost at all, because the cloth was never outside what friction could hold. What the plot cannot show is time: nothing here says how long the rearrangement takes, only where it stops.

A tensioned cloth loses its load

Clamp a fabric at a fixed length and its tension falls overnight. Nothing crept and nothing flowed: the crossings rearranged locally until the load had dropped to what friction alone can hold, and that level is the same number whatever the cloth was pulled to — so the harder it was tensioned, the smaller the share it keeps.

mechanics · Set The strain at a fold against the strain each fibre breaks at. For each fibre, the surface strain at the sharpest fold a 20 tex yarn of it can make — which is √(packing × fibre tex ÷ yarn tex), with no measurement of a crease in it — beside its own measured breaking extension. cotton and flax are strained past the low end of their breaking range, so some of their fibres break at the fold, and that is what a linen crease is. The rest survive, and among them viscose and wool return less than three fifths of what they were given, which is the other way a cloth creases. Both columns are needed: viscose survives with a factor of two to spare and is among the three worst by measurement. What the bars cannot show is wool, which the census puts in the wrong column because the recovery figures are the immediate ones and wool's is the most delayed of any fibre here.

Which fibres crease, and why there are two answers

Run the sharpest fold a yarn can make against every fibre's breaking extension and its recovery, and the ranking that falls out is the trade's own — linen worst, cotton next, wool and the melt-spun filaments best. It falls out of two columns rather than one, because two fibres in the bottom three get there by different mechanisms, and a treatment that fixes one does nothing for the other.

finishing · Crease What a knit gives when it is pulled. Force against course-wise extension for a 20 tex cotton jersey at a 3.5 mm loop, computed from the loop's own bending with the relaxed shape as the yarn's natural one. The loop length is the same at every point on the curve: nothing here is the yarn stretching. It reaches 92% extension at 2.96 N per metre and then stiffens by a factor of 85 over the rest of the range, as the straight line between two interlacings runs up against the yarn between them. This is the number the collection's second phase recorded as a lower bound it could not compute, and it is still a lower bound in one respect: friction at the contacts is not in it, so a real fabric is stiffer than this and does not come back along the same curve.

A loop is set and not sprung

The way out of a model that predicts a jersey should spread is to stop treating its yarn as a straight rod bent into a loop. A yarn that has been wetted, heated and dried has taken the loop as its own natural shape — and once the natural shape is the loop, every force downstream becomes computable with the relaxed fabric as the origin.

finishing · Elastica A knitted loop is a plane curve in a plane that is not the fabric's. A relaxed 20 tex jersey at a 3.5 mm loop, seen from the end of a course. Each course is a straight line because it is one: a half period leaves and arrives along the course direction, so the plane it bends in contains that direction, and a plane curve seen along a line in its own plane projects to a segment. The upper panel expands the thickness 3× so the arrangement can be seen and no angle may be measured off it; the lower panel is the same fabric at one scale, where the tilt is what it really is. The angle is 11.75°: a climb of one yarn diameter, 0.167 mm, against a drop of a course spacing and a diameter, 0.803 mm. Successive courses overlap by exactly one diameter, which is the interlacing, and the fabric is therefore 0.334 mm thick — two yarn diameters, with nothing fitted.

A state is a thickness too

This collection's rule is that a fabric dimension quoted without its relaxation state is not a measurement. A knitted fabric has three dimensions and only two of them obey the rule: its thickness is the same in every state, because the interlacing that sets it does not relax.

finishing · State What leaving the plane costs, which is less than nothing. Bending energy a stitch against how far the yarn climbs between one interlacing and the next, for a 20 tex cotton jersey at a 3.5 mm loop. The curve falls. A climb is not an extra bend added to a curve that was otherwise unchanged; it is part of the straight line the thread has to span, so a longer climb leaves less slack to be spent on curvature. At a jersey's own climb of one diameter the energy is 24395 nJ against 25060 for the planar model — 2.7% lower, where an earlier estimate on this site put the ride at three per cent of the loop's bending and had the sign the other way round. At a rib's climb of three or four diameters the fall is 33%.

A rib's relaxation is not its bending either

A jersey does not settle where its bending energy is least, and this collection has said so for several rungs. A rib does not either, and the model now says how far from least it would have to go: sixteen yarn diameters of bed gap before the yarn runs out, against the two or three a machine is set to.

finishing · Shrinkage How much of a yarn has to hang before it stops snarling. The tension a 20 tex cotton needs to stay straight, at each twist level, expressed as the length of the yarn's own weight that would supply it. The two curves are the two ends of the stiffness bracket: the fibres free to slide, and the section coherent. At 800 turns a metre they are 1.9 metres and 616. Anybody who has let go of a twisted yarn knows which of those is right, which makes this one of very few places where the bracket can be closed from the everyday end. Both rise as the square of the twist, because the torque does and the criterion is quadratic in it.

A yarn that has been set has no torque

Every torque on the torsion ladder assumes a yarn is elastic in twist for ever. It is not: a steamed yarn's residual torque is gone, its twist is unchanged, and the process that removes one without the other is the trade's whole answer to liveliness.

finishing · Memory A slack twisted yarn takes a coil of one size. A 20 tex cotton at 800 turns a metre. Its own torque is 1.177 µN·mm at the free bound, and a rod under tension T is stable while its torque stays under 2·√(B·T). Below that tension the straight state stops being a minimum and the thread wraps on itself at a radius of 1.59 mm. That radius is 2B/M, which is 2/(r·ω) once the torque is written out: it depends on the twist and on the ratio of the two stiffnesses, and on neither stiffness itself.

The twist a fabric gives back

A T-shirt that hung straight in the shop has its side seam round the front after three washes. The torque was there all along, the setting had hidden it, and the water gave it back — which makes spirality a finishing failure rather than a knitting one.

finishing · Memory How hard a fabric is to bend, per unit width. Bending rigidity in micronewton metres per unit width, computed the same way for eight woven cloths and for a jersey in each of its two directions: the yarn's own rigidity, times the length of yarn per unit area, times the fourth power of the cosine of the angle each element makes with the bending direction. The knit lands inside the band of the woven cloths rather than below it, which is worth knowing because a knit is usually called the softer fabric. It is not softer to bend; it is softer to stretch, by three decades. What it does have is direction: 2.17 to one between its two axes, where a balanced plain weave is near one, and the soft axis is the one a jersey rolls about at its top and bottom edges.

What friction has to hold in a relaxed knit

A knit's bending energy slopes away from the fabric everybody measures, so something is holding it there. Along its courses friction holds comfortably. Along its wales the driving force is exactly the contact force, so the whole balance collapses to one condition — the friction coefficient must exceed a half — and no yarn in this collection reaches it.

mechanics · Friction

Named alongside it

The objects these essays reach for when they reach for this one.

RelaxationElastic recoveryDimensional stabilityInterchange budgetContact forceCrimp interchangeSpecificationTensile locusYarn frictionBending rigidityFibre finenessJamming