Damage — where it appears

What wear takes out of a cloth, as distinct from what it takes off. Mass loss understates it, because material comes off every thread at its thinnest place — and the first material off any fabric is its hair layer, which was carrying nothing at all.

Named by 6 essays across one field — each of them below, with the objects they name alongside it.

A cloth loses its strength long before it loses its mass. Rubbing a 2/2 twill in sheeting down, plotted against how much of its own solid volume has gone. The lower curve is the fraction of the plan the rubbing is touching; the upper is the fraction of the warp's section that has been cut away. They are wildly different because the wear is spread and the damage is concentrated: material comes off the whole surface, but it comes off every thread at the same place, and a thread breaks at its thinnest place. At one per cent of the mass gone the section is already 5% smaller. That is why a fabric that looks barely worn fails a strength test, and why abrasion resistance measured as mass loss and abrasion resistance measured as residual strength are two different quantities that are quoted as one.

A cloth loses its strength before its mass

Rub a fabric and it sheds material from all over its surface, but it sheds it from every thread at the same place — and a thread breaks at its thinnest place. So the strength gone is always several times the mass gone, the ratio is computable from the bearing curve, and it is worst for the weave whose crowns are points.

applied · Damage How much of an abrasion loss is not damage. The share of a reported abrasion mass loss that is hair rather than cloth, for sheeting as woven and raised 64-fold. The first material off a fabric is its hair layer, which is 0.107% of a bare cloth's mass and 6.84% of a napped one's — and which regenerates, so it keeps coming off. A bare cloth is through it by 5344 cycles and the test then reaches the crowns, where the loss means damage. A napped cloth is not through it by 342000, which is more cycles than any standard test runs, so a Martindale on a fleece never measures the fabric at all. Two cloths taken to the same mass loss have therefore not lost the same thing, and the more heavily napped one may not have been damaged. a-cloth-loses-its-strength-before-its-mass made the same point about a different pair of quantities; this is the same failure one layer further out.

Abrasion takes the hairs first

An abrasion test reports milligrams lost against cycles, and the first milligrams off any fabric are not fabric. On a bare cloth that stage is over in a few thousand cycles. On a napped one it is not over by the end of the test, so a Martindale on a fleece never measures the fleece.

applied · Damage A knot, and the tension falling through it. A 20 tex cotton thread wrapped through 1 turn at a bend radius of 1 yarn diameters, with a coefficient of friction of 0.30. The wrap is drawn as a spiral because a thread taken round a pin comes back beside itself rather than onto itself. The marks round it are the fraction of the entry tension still there: 100%, 69%, 47%, 32%, 22%, 15%. The bend has already spent 3.6% of strain at the outside of the thread before any of that happens, against a breaking strain of 6.6%. So the largest total is at the entry, before the knot has done any gripping at all — which is where a knot in a real yarn is observed to break, and why a knot's efficiency is a property of its first bend rather than of the knot.

A knot is nothing but contact

A knot has no fastening in it. Nothing is glued, hooked, sewn or threaded through a hole: a thread is bent round itself until the friction where it presses on itself is more than the load. That makes a knot the purest contact problem in the subject, and the place to look first for what contact does.

applied · Contact A knot, and the tension falling through it. A 20 tex cotton thread wrapped through 1 turn at a bend radius of 1 yarn diameters, with a coefficient of friction of 0.30. The wrap is drawn as a spiral because a thread taken round a pin comes back beside itself rather than onto itself. The marks round it are the fraction of the entry tension still there: 100%, 69%, 47%, 32%, 22%, 15%. The bend has already spent 3.6% of strain at the outside of the thread before any of that happens, against a breaking strain of 6.6%. So the largest total is at the entry, before the knot has done any gripping at all — which is where a knot in a real yarn is observed to break, and why a knot's efficiency is a property of its first bend rather than of the knot.

Where a knot breaks

It breaks at the entry, before the knot has done any gripping at all. Two quantities run along a knot's path and only one of them rises; the other falls from the first millimetre; and their sum is largest where the thread arrives.

applied · Damage What a knot costs, and what decides it. Knot efficiency against the radius the thread is bent to, for 5 fibres at 20 tex, computed at the free end of the stiffness bracket — each fibre bending about its own axis, so the strain at the outside of the bend is half a fibre diameter over the radius. At one yarn diameter of radius, cotton keeps 46%, which is the rule of thumb that a knot halves a rope's strength. What separates the curves is not the knot and not the friction: it is the fibre's own breaking strain, which is how much the bend is allowed to spend before there is nothing left.

A knot halves a yarn and says why

The rule is quoted for every rope and every knot and derived nowhere. It comes out at forty-six per cent for a cotton — but only if the yarn's fibres bend individually. A yarn bending as a solid section has already spent five times its breaking strain before any load arrives, so it could not be knotted at all.

applied · Tensile What a knot costs, and what decides it. Knot efficiency against the radius the thread is bent to, for 5 fibres at 20 tex, computed at the free end of the stiffness bracket — each fibre bending about its own axis, so the strain at the outside of the bend is half a fibre diameter over the radius. At one yarn diameter of radius, cotton keeps 46%, which is the rule of thumb that a knot halves a rope's strength. What separates the curves is not the knot and not the friction: it is the fibre's own breaking strain, which is how much the bend is allowed to spend before there is nothing left.

Which yarns knot well

A knot's efficiency depends on three things and only one of them is the knot. The other two are the fibre's fineness and its breaking strain, and across this collection's own table those give efficiencies from six per cent to eighty-three at exactly the same bend.

applied · Tensile

Named alongside it

The objects these essays reach for when they reach for this one.

TenacityContactFibre countAbrasionBending rigidityCapstanFibre finenessFrictionMeasurementPacking factorReal contact areaBearing curve