The energy well, and where the cloth sits in it. The bending energy of a sheeting at every state on its own constant-thread-length locus, plotted against how the crimp divides between the two systems. The minimum is at 1.22 and the value every Peirce solution here is drawn at is 1.00, marked. The well's depth decides how firmly the ratio is settled, which is why an open scrim's measured crimp scatters and a close sheeting's does not. What the plot cannot show is the friction that stops a cloth reaching the bottom, which turns the minimum into a band.

The crimp ratio is not a measurement

Peirce's geometry is two thread systems, four unknowns and three equations. It cannot say how the crimp divides between warp and weft, so every cloth solved so far has been drawn at a ratio somebody chose. Give the threads a stiffness and the missing equation arrives — and for six of the eight cloths in the table it arrives with no material constant in it at all.

setting · Crimp The load–extension curve, computed from a stiffness. The tension in one end of a sheeting against how far the cloth has been extended, computed as the slope of its bending energy along its own constant-thread-length locus. The curve passes through zero at the state of least energy, which is where an unloaded cloth sits, and rises either side of it. What the curve cannot show is what happens after the crimp runs out: past the end of the locus the load is carried by stretching yarn rather than by straightening it, and that is a modulus three orders of magnitude higher and a different figure.

The locus gets a force

This site has drawn the set of states a cloth can reach without stretching any yarn, and has never been able to say which of them it is in or what it would cost to move. Both questions are one derivative of a bending energy — and the answer explains the flat start every fabric's load–extension curve has, which is not slack yarn but a symmetry.

mechanics · Tensile A crossing before and after it is pressed. One warp end of a sheeting riding over three picks, drawn twice to the same scale. Unpressed, both sections are circles and the cloth is 0.388 mm thick. At 0.40 N per crossing the sections flatten to aspect ratios of 1.75 and 1.84, the cloth thins to 0.263 mm, and the warp runs flat for 0.109 mm over each pick before it begins to curve. What the drawing cannot show is why the cloth does not do this by itself: flattening shrinks the arc radius as well as the crimp height, so it costs bending energy, and a relaxed cloth keeps its threads round.

A flattened thread is a record of a force

A yarn in cloth is not round, and this site has modelled the flattening for as long as this collection has run with the amount of it left as a number somebody chose. Give the section a stiffness and ask what the cloth prefers, and the answer is a circle — at every stiffness, for every balanced cloth in the table. Flattening does not happen by itself; it happens because something pressed.

mechanics · Compression The crimp ratios a dense shirting can have. Poplins in 15 tex warp and 20 tex weft at 22 picks, from 32 ends per centimetre to 52. Each bar is the interval of warp-to-weft crimp ratios the construction admits at all: the warp must supply at least the thickness the weft cannot reach, and at most what it can reach itself. The rule at one is this site's standing default. It sits inside the interval up to 44.18 ends per centimetre and outside it beyond — so for a dense shirting an equal division of the crimp is not merely the wrong assumption but a geometric impossibility. The 44-end poplin this site's own cloth table called impossible for a long time sits a fifth of an end below that limit, which is why the solver failed on it: its feasible interval was real and narrow, and a bisection on the whole range walked away from it.

The cloth that was called impossible

This site's own table of fabrics carries a note saying a real 44-end poplin has no solution in its geometry at all, and that the poplin row was therefore set at 32 ends. The cloth solves. What had no solution was the search — a bisection that treated a state it could not reach as evidence of having gone too far, and walked away from the answer every time.

setting · Crimp

Named alongside it

The objects these essays reach for when they reach for this one.

Bending rigidityJammingSpecificationYarn diameterCrimpCrimp heightCrimp interchangeInextensiblePacking factorPeirce's geometrySettTensile locus

All concepts