Textile Structure
how cloth is put together
Concept

Compression energy — where it appears

What it costs to change a thread's section from round to flat, at constant area, against the fibre's transverse stiffness. Adding it to the bending energy is what turns Peirce's circle and Kemp's racetrack into one fabric before and after something pressed it.

Named by 14 essays across 5 fields — each of them below, with the objects they name alongside it.

The step between a figure and its ground. Three figures on a plain ground, all in one sheeting's threads at its own setts. A thread presses on the thread it crosses only where it turns, and it turns at its interlacings — so the pressing a region receives per unit area is the contact force at one turn times the turns per unit area, and the second factor is a property of the matrix exactly. A five-end satin turns two fifths as often as a plain weave, is pressed two fifths as hard, flattens less, and stands 55 µm proud of it. What the rows cannot show is that both regions are given a plain weave's weave angle: a satin's crimp is genuinely smaller and its turns genuinely gentler, so the real step is larger than this, by an amount not computed here.

A figured cloth has a step in its surface

A damask is one cloth in one set of threads at one sett, and it is not flat. A thread presses on the thread it crosses only where it turns, so a region that turns less often is pressed less often, flattens less and stands thicker — and the step is a ratio of interlacing rates, read off the matrix with no yarn property in it.

pattern · Blocks A crossing before and after it is pressed. One warp end of a sheeting riding over three picks, drawn twice to the same scale. Unpressed, both sections are circles and the cloth is 0.388 mm thick. At 0.40 N per crossing the sections flatten to aspect ratios of 1.75 and 1.84, the cloth thins to 0.263 mm, and the warp runs flat for 0.109 mm over each pick before it begins to curve. What the drawing cannot show is why the cloth does not do this by itself: flattening shrinks the arc radius as well as the crimp height, so it costs bending energy, and a relaxed cloth keeps its threads round.

A flattened thread is a record of a force

A yarn in cloth is not round, and this site has modelled the flattening for as long as this collection has run with the amount of it left as a number somebody chose. Give the section a stiffness and ask what the cloth prefers, and the answer is a circle — at every stiffness, for every balanced cloth in the table. Flattening does not happen by itself; it happens because something pressed.

mechanics · Compression A crossing before and after it is pressed. One warp end of a sheeting riding over three picks, drawn twice to the same scale. Unpressed, both sections are circles and the cloth is 0.388 mm thick. At 0.42 N per crossing the sections flatten to aspect ratios of 1.79 and 1.88, the cloth thins to 0.260 mm, and the warp runs flat for 0.113 mm over each pick before it begins to curve. What the drawing cannot show is why the cloth does not do this by itself: flattening shrinks the arc radius as well as the crimp height, so it costs bending energy, and a relaxed cloth keeps its threads round.

Peirce and Kemp are one cloth at two moments

This site has run two thread sections side by side since the setting field was built — a circle and a flattened racetrack — and said honestly that they disagree and that the disagreement is the point. They are not rival descriptions of the same fabric. They are descriptions of the same fabric before and after something pressed it, and the difference between them is a pressure that can now be named.

setting · Sett The bracket that closes and the bracket that does not. A 25 tex cotton yarn at a packing factor of 0.6. Its bending rigidity lies between 0.00117 N·mm² — the sum of its fibres', with them free to slide — and 0.478, a solid rod of its own diameter: a factor of 408, and both ends are derivations. Its resistance to being squashed out of round has an upper bound of the same kind, 369 N/mm² for a solid section, and no lower bound at all, because fibres free to slide resist a change of shape with nothing. That is why the aspect ratio of a flattened yarn has been a free parameter here since the setting field was built: a quantity bounded below by zero cannot be estimated from its bounds, and has to be measured.

The stiffness with no lower bound

A yarn's bending rigidity lies between two derivable ends and the ratio is the fibre count — wide, but closed. Its resistance to being squashed out of round has an upper bound of the same kind and a lower bound of exactly nothing, because fibres free to slide resist a change of shape with nothing at all. That is why nobody could ever compute the aspect ratio of a flattened thread.

mechanics · Compression From a calender's line load to a force at one crossing. A sheeting through a nip loaded at 30 N per millimetre of bowl width, with the cloth in contact over 5.0 mm. The pressure is the first divided by the second, 6.00 N/mm², and the force at one crossing is that pressure times the area a crossing owns — the product of the two thread spacings, 0.1374 mm². So the crossing carries 0.824 N, the sections flatten to 2.42 and 2.63, and the cloth thins from 0.388 mm to 0.218 mm. What the drawing cannot show is that two cloths through the same nip are not given the same treatment: the area a crossing owns varies fivefold across this site's table, and it is a factor in the force.

A calender spends the compression for good

Calendering was described on this site as moving a cloth from one thread-section model to another, which was right and had no number in it because the amount of the move was a free parameter. It is a pressure now — and the same nip setting turns out to give two cloths quite different treatments, because the force at a crossing is the pressure times the area a crossing owns.

finishing · Lustre finish How much too thick a round section is, and what reconciles it. For each cloth in this site's table: the thickness a circular Peirce section predicts, the thickness a cloth of that construction measures, and the force per crossing that makes the flattened model reproduce the measurement. The over-prediction runs from 36% to 81%. The reconciling forces span a factor of 4.6 across a table whose counts span a factor of six, and every one of them is of the order of the contact force the cloth's own warp tension supplies — which is what makes this a model rather than eight fitted parameters. What the rows cannot show is that the thicknesses are trade figures for cloths of these constructions rather than measurements of these particular fabrics, so what is being read is an ordering.

The relaxed cloth's contact force

How hard two threads press on each other in a cloth that is not being pulled is the number this site's own integrity criterion has needed since its first essays, and the route to it was an elastica nobody had. A thickness gauge supplies it instead — because a cloth's thickness is a record of how flat its threads are, and how flat they are is a record of how hard they are pressed.

mechanics · Compression An operation multiplies a spread by its own log-slope. A transformation does not leave a population's spread alone: if y goes as the kth power of x then a small spread in x becomes k times that spread in y, exactly in the limit and nearly so at the CVs a yarn has. So an operation with an exponent below one narrows the population it acts on — a thickness that goes as the square root of a load comes out at half the spread it went in with — and one with an exponent of four widens it fourfold. This is the same derivative that decided every bias in this ladder, read for its magnitude rather than for its curvature, and it is why a finish can be a variance-reducing operation without anyone having chosen it for that. The straight line through the origin is the whole of the rule; the departure from it at the right-hand end is the second-order term arriving, which is where the linearisation stops being one.

A finish spends a spread before it spends a mean

Every operation on a cloth multiplies the variation it inherits by its own log-slope, so an operation with an exponent below one makes the cloth more even and one above it makes the cloth less even. Calendering, which is bought for evenness, has an exponent of 1.4.

finishing · Lustre finish The crossings under a 25 mm² presser foot. A 25 mm² foot on a muslin covers 12 ends and 11 picks, which is 132 crossings — and a first guess treats those as 132 chances of finding a thick place. They are not independent chances. Every crossing along one end shares that end's diameter, so the largest crossing is the largest end plus the largest pick, and the number of tries is 23: the threads. Each cell here is shaded by its own two diameters, and the darkest is at the meeting of the darkest row and the darkest column, which is what that identity looks like. The gauge rests on it and reads 0.431 mm, against 0.342 for the cloth's mean crossing — 26% over.

A thickness is a maximum, not a mean

A presser foot rests on whatever is highest beneath it, so the thickness of a fabric is an extreme value — and an extreme grows with how much cloth is asked. The standard specifies the foot's area because the foot's area is in the answer.

mechanics · Compression A calender multiplies the highlight by 32, and all of it is width. A 2/2 twill in sheeting pressed at increasing force, with the specular area recomputed at each state from the site's own compression model. It rises from 0.91% of the plan to 28.9%, a factor of 32, while the cloth thins from 381.6 µm to 186.1 µm. The gain is not in the length of the crowns: that moves by 5 per cent. It is in their width, which moves by 31.8 times, because pressing puts a flat top on the section and a flat top has one normal rather than a fan of them. The finish does not polish the thread. It changes the dimension of the highlight, from a line to a band, and the arithmetic says so by refusing to put any of the gain in the other factor.

A calender buys the width

Press a cloth and its lustre multiplies by twenty-four. None of that comes from the length of its crowns, which moves by six per cent; all of it comes from their width, because a flattened section has a plane on top of it and a plane has one normal rather than a fan of them. The arithmetic refuses to put any of the gain in the other factor.

weaves · Shine Two exponents in a compression curve. How far a flat plate sinks into plain, 2/2 twill, satin 8 in sheeting, against the pressure it is applying, on logarithmic axes where a power law is a straight line. The measured slopes over the light end of the range are 0.50 for the plain, 0.67 for the 2/2 twill, 0.67 for the satin 8 — against two thirds predicted for any weave carrying a float and one half for a weave carrying none. The prediction is one line of algebra: pressure is a stiffness times a strain times a bearing fraction, the bearing fraction is a square root of depth for a plateau and linear in it for a point, so the pressure is the three-halves power in the first case and the square in the second. Nothing is fitted to produce it; the slopes are measured afterwards and compared. At the heavy end every curve bends, because the crowns have merged and the cloth has stopped being a surface and started being a solid — which is a different regime with a different law, and it belongs to the compaction of a fibre mass rather than to the geometry of an interlacement.

A cloth compresses along its own bearing curve

A fabric's pressure–thickness curve is always fitted with an empirical power law and the exponent is reported without explanation. It is not empirical. At light loads it is two thirds for any weave carrying a float and one half for a weave carrying none, and the two numbers come out of one line of algebra with nothing fitted in it.

mechanics · Compression A thickness is a property of the pressure it was measured at. What a gauge reports for sheeting against the pressure it presses with. At 1 kPa it reads 0.382 mm, which is the cloth; at 0.02 kPa it reads 0.555 mm, which is the cloth plus 87 µm of hair on each face. The difference is 31% of the reading and it is not a compressibility: nothing in the fabric has been squashed, the foot has simply stopped in a different place. That is why every thickness standard specifies its pressure to two figures, and why comparing a thickness from one standard with a thickness from another is comparing two different measurements of two different objects. The dashed line is the cloth's own geometric thickness, which no reading below the crossover ever reaches.

A compression curve is two laws in series

A published fabric compression exponent is a fitted number with no derivation attached, and this site has already said why: the range it is fitted over straddles two regimes. One of them turns out not to be in the cloth at all.

mechanics · Compression The force at an interlacing, which no longer lies in the fabric. A crossing of a relaxed jersey in section on the left, with the thickness expanded 3×, and on the right the contact force drawn at the angle the solve gives it — which is a true angle, unlike anything in the section beside it. The head of one course and the feet of the next lie one yarn diameter apart through the fabric, 0.167 mm, so the interlacing is not a point in a plane and the force at it is not in one either. It comes out at 38.30 mN a stitch, turned 11.75° out of the fabric: 37.50 mN along the wales, which is what friction has to hold, and 7.81 mN through the thickness, which is what holds the two faces apart. Divided by the area a stitch occupies the second is 15.1 kPa, or 113 mmHg — a pressure, and the quantity a compression measurement reports.

The force that holds a knit open

Resolving a knitted loop's contact force out of the fabric's plane leaves a fifth of it pointing through the thickness. That fifth is 7.8 millinewtons a stitch, fifteen kilopascals over the area a stitch occupies, and it is the whole reason a jersey has a thickness rather than a plan.

mechanics · Elastica What leaving the plane costs, which is less than nothing. Bending energy a stitch against how far the yarn climbs between one interlacing and the next, for a 20 tex cotton jersey at a 3.5 mm loop. The curve falls. A climb is not an extra bend added to a curve that was otherwise unchanged; it is part of the straight line the thread has to span, so a longer climb leaves less slack to be spent on curvature. At a jersey's own climb of one diameter the energy is 24395 nJ against 25060 for the planar model — 2.7% lower, where an earlier estimate on this site put the ride at three per cent of the loop's bending and had the sign the other way round. At a rib's climb of three or four diameters the fall is 33%.

What a knit gives up when it is pressed

The woven half of this collection has had a compression curve for several rungs — a thickness that falls under load, a bearing area that grows, a pressure at every point. The knitted half had a plan and no depth. It has a relaxed thickness and an initial slope now, and the two fabrics turn out to resist for different reasons.

mechanics · Compression What flattening costs, against what the loop's bending is worth. The energy of squashing a 20 tex cotton to the 78% the fabric's geometry demands, as a multiple of the whole bending energy of one stitch, at three lateral rigidities. The free bound is exactly zero: a bundle of fibres free to slide resists a change of shape at constant area not at all, so flattening is free and the bracket on it has no floor. The coherent bound is 36 times the loop's bending, so a yarn that could not rearrange could not be knitted into this fabric at all. The fabric flattens, so it is reading the free end — which is the fourth ordinary observation on this site to land at that end of the bracket.

Flattening is free and impossible

The fabric demands a flattening and the yarn has to supply it. At one end of this collection's oldest bracket the deformation costs exactly nothing; at the other it costs thirty-six times the whole bending energy of a stitch. The fabric flattens — which is the fourth everyday observation in one phase to land at the same end.

mechanics · Contact

Named alongside it

The objects these essays reach for when they reach for this one.

Cloth thicknessContact forceSpecificationContact pressureJammingRacetrackYarn diameterBearing curveCalenderingElasticaFrictionPacking factor