Viscose — where it appears

Regenerated cellulose, which shares cotton's density and modulus and is indistinguishable from it in every geometric result here. Water separates them twice, by swelling nearly twice as far and by losing half its strength where cotton gains a tenth.

Named by 3 essays across 2 fields — each of them below, with the objects they name alongside it.

A cotton fibre dry and wet. One cotton fibre in its dry state and saturated with water, both drawn at the same scale in both directions. It is 20% wider and 1.2% longer, so its cross-sectional area rises by 44% if the section stays similar to itself. The length difference is drawn and is nearly invisible, which is the point: a swelling that were the same in both directions would make a cloth bigger and change nothing about its structure, and this one changes every ratio of a diameter to a spacing in the cloth. What the drawing cannot show is the section: a cotton fibre is not a cylinder, and the directly measured area swelling of 40% to 42% does not agree with the square of the width change, which is a fact about the fibre.

What water does to a thread

A cotton fibre in water is a fifth wider and a hundredth longer. If it grew equally in both directions a wet cloth would simply be a bigger cloth and nothing structural would follow; because it does not, every ratio of a diameter to a spacing in a cloth moves, and they all move the same way.

cloth · Water A yarn's voids against its fibres' swelling. One cotton yarn's cross-section at a packing factor of 0.60, drawn dry and with every fibre swollen by 20% while the yarn's own outline is held. The fibres now occupy 0.864 of the section, which is above the 0.75 a heavily compacted assembly reaches and above the 0.65 of a spun yarn, so the yarn cannot stay this size: it must grow by at least 7.3%. What the drawing cannot show is disorder — the fibres are laid on a lattice here to make the areas exact, and a real yarn's fibres are neither round nor evenly spaced, which is why the bound is quoted over three packing limits rather than at one.

A yarn's voids are not enough

A ring-spun cotton yarn is sixty per cent fibre and forty per cent air, and its fibres gain forty-four per cent of area in water. The obvious thought is that the air takes it. The arithmetic says the air cannot, and gives a floor on how far the yarn itself must grow with no measurement of a yarn in it anywhere.

cloth · Water Cotton and viscose in every column this site carries. The two cellulosic fibres compared across every constant on this site. Both are cellulose at 1.52 g/cm³, both are given a modulus of 8 GPa and a fineness of 1.7 dtex, so a 20 tex yarn of either has the same diameter to the last figure — and therefore the same crimp, the same cover, the same jamming sett and the same bending bracket. Every geometric result on this site is the same number for the two fibres. Water separates them twice: viscose swells 1.75 times as far across and loses half its strength where cotton gains a tenth. What the table cannot show is why, which is a question about how cellulose is arranged inside a fibre and is not in this collection.

Water tells two fibres apart

Cotton and viscose are the same material by every constant this collection carries. Same density, same modulus, same fineness, so the same diameter at every count and the same crimp, cover, jamming sett and bending bracket. A wash separates them by a factor of two, and it is the only thing here that can.

mechanics · Yarn stiffness

Named alongside it

The objects these essays reach for when they reach for this one.

Fibre diameterMoisturePacking factorSwellingRegainAnisotropyBending rigidityBoundBracketCompactionCover factorCrimp