Textile Structure
how cloth is put together
Generator

A fibre's two stiffnesses, as the ratio that survives the bracket

A fibre's two stiffnesses, as the ratio that survives the bracket
A fibre's two stiffnesses, as the ratio that survives the bracket. C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it.

C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it.

13 essays call torque-bars. The drawing above is what it returns with no arguments at all; every call below passes it something, because a placement that passes nothing draws whichever member of the family the generator happens to default to rather than the weave its essay argues about.

Where it is called

Changing this generator changes every one of these figures.

The fold the trade actually makes. 2 singles of 20 tex cotton at 800 turns a metre, folded at 566 — a ratio of 0.707. That is 1/√2, the ratio at which the fold's surface helix angle equals its singles' — 22.8° — because a fold of 2 singles is √2 times the diameter. The trade's own bracket for 2 folds is 0.6 to 0.75, and it contains this number. Compound and figured cloths

A leno twists what a weave only crosses

Every woven cloth's threads have a linking number of zero, and that is why an open cloth slips. A leno is the one woven structure whose warp ends wind about one another, so it is the one whose threads are linked — and it is famously the structure that holds at setts where nothing else does.

 Unlinked: a woven crossing: as close as anybody likes, and never through. Two closed curves and the Gauss linking integral taken over them, which returns 0.0000 at 200 segments a curve. A woven crossing: as close as anybody likes, and never through. A linking number is an integer, so a value coming back at a few thousandths of one is the discretisation reporting itself rather than a fabric that is slightly linked. The two arrangements are the two ways of making cloth: a knitted fabric's courses link and a woven cloth's threads do not, at any crimp and for ever. Compound and figured cloths

A braid is a third way to hold threads

Weaving holds by friction and knitting holds by linking. A braid does neither: its strands travel across the structure and back, so no pair of them is linked and no pair of them returns to where it started — and it holds without a reed, a beat-up or a sett.

 A knitted interlacing, and the number that makes it a fabric. Two loops idealised to rings, one drawn through the other, which is what a needle does. The Gauss linking integral returns 1. A knitted fabric of n wales has that between every pair of adjacent courses n times over, and it is the whole of why a knitted fabric can be made from one thread and taken apart by pulling it. What cloth is

Why a knit runs and a weave frays

The two fabrics fail in two ways and everybody knows which is which. This collection has described both accurately for eighteen phases without being able to say what causes them, and the cause turns out to be one integer each: nought for a cloth, one per wale for a knit.

 A woven crossing, and the number that never changes. A warp end and a weft pick at 6% crimp, drawn with the thickness expanded three times so the interlacing can be seen. Each goes over its neighbour and comes back; neither passes through the other. The Gauss linking integral over the pair, closed far outside the crossing, returns 0.0000. It returns that at every crimp and for every weave, because crimp moves a thread up and down across its neighbour and a curve that goes over and comes back has done nothing a linking number can see. Weaves

A woven cloth is not linked at all

Every thread in every woven cloth passes over its neighbours and comes back. None of them passes through. So the linking number of any two threads in any weave is zero, at any crimp, permanently — and almost everything a cloth does that a knitted fabric does not follows from that one number being nought.

 What links what, in the two ways of making cloth. The linking number between two adjacent courses, for a knitted tube of 12 wales, for the same tube as this collection's model draws it, and for a woven cloth's two thread systems. The fabric's is 12 — one for every needle loop drawn through the loop below. The model's is -0.0000, because it places the interlacing at a point where two centre lines pass a diameter apart and two curves passing beside one another are not linked. The woven cloth's is -0.0000 and always will be, at any crimp and for every weave. That last row is not a defect of any model: a woven cloth really is unlinked, and it is the reason it frays where a knitted fabric runs. Knits and other structures

A point cannot link

A knitted fabric of n wales has a linking number of n between every pair of adjacent courses. This collection's model of the same fabric has zero, and it has zero because the interlacing was declared to be a point where two centre lines pass a diameter apart — which is a near miss, and a near miss is not a knot.

 Three rules for how hard to fold a yarn, and which one the trade uses. For 2, 3, 4 folds of 20 tex cotton at 800 turns a metre: the ratio that makes the fold's surface helix angle equal its singles', the ratio that sets the fold's net moment to zero, and the ratio the trade actually folds at. The surface rule is 1/√n exactly, because a fold of n singles is √n times the diameter. The torque balance is C/(B+C), which for this fibre is 0.201 and is the same at every count, every twist and every number of folds. The trade's brackets contain the surface rule in all three rows and the torque balance in none of them. Setting and geometry

The folding rule is a surface angle

Fold at two thirds for two singles, six tenths for three, a half for four. Those are one over the square root of the fold count, they are what makes a fold's surface twist angle equal its singles', and all three of the trade's brackets contain the number exactly.

 The fold the trade actually makes. 2 singles of 20 tex cotton at 800 turns a metre, folded at 566 — a ratio of 0.707. That is 1/√2, the ratio at which the fold's surface helix angle equals its singles' — 22.8° — because a fold of 2 singles is √2 times the diameter. The trade's own bracket for 2 folds is 0.6 to 0.75, and it contains this number. Setting and geometry

What a balanced yarn is balanced about

A specification that says a yarn is balanced does not say which of two conditions it means, and the two have different numbers, different dependences and different consequences. One of them is what folding achieves and the other is what folding is said to achieve.

 Three rules for how hard to fold a yarn, and which one the trade uses. For 2, 3, 4 folds of 20 tex cotton at 800 turns a metre: the ratio that makes the fold's surface helix angle equal its singles', the ratio that sets the fold's net moment to zero, and the ratio the trade actually folds at. The surface rule is 1/√n exactly, because a fold of n singles is √n times the diameter. The torque balance is C/(B+C), which for this fibre is 0.201 and is the same at every count, every twist and every number of folds. The trade's brackets contain the surface rule in all three rows and the torque balance in none of them. Setting and geometry

A cabled yarn is a fold of folds

The rule that sets a fold's twist is one over the square root of the number of components. Apply it twice and a cabled yarn's three twist levels are fixed by two integers — which is a prediction with no free constants, about a class of yarn the trade quotes no rule for at all.

 A knitted interlacing, and the number that makes it a fabric. Two loops idealised to rings, one drawn through the other, which is what a needle does. The Gauss linking integral returns 1. A knitted fabric of n wales has that between every pair of adjacent courses n times over, and it is the whole of why a knitted fabric can be made from one thread and taken apart by pulling it. Knits and other structures

A tuck is the one stitch that links twice

Knitting has three stitches and only one of them makes a new link. A knit stitch links a loop to the loop below; a miss links nothing; and a tuck holds two loops in one head — which is why a tuck stops a run and why the three cannot be described by one number.

 A fibre's two stiffnesses, as the ratio that survives the bracket. C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it. Mechanics and drape

A thread has a second stiffness

Every mechanical number here came from one material constant: how hard a thread is to bend. A thread also resists being twisted, nothing here has ever used that, and the ratio between the two turns out to be the only stiffness number about a yarn that can be known at all.

 A fibre's two stiffnesses, as the ratio that survives the bracket. C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it. Mechanics and drape

The one fibre whose answer is known

A table of measured constants is worth what its worst row is worth, and nobody can tell which row that is. This one has a member whose answer was known before anybody measured it, and the ordering of the other nine turns out to say something about how fibres are made.

 Two stiffnesses, one bracket, and a ratio that does not move. The bending and torsional rigidities of a cotton yarn against its count, each drawn at both ends of its own bracket, on a logarithmic scale. The four curves are two parallel pairs: the torsional bracket is the bending bracket exactly — the fibre count over the square of the packing factor, 327 at 20 tex — so the vertical gap between the two bounds is the same for both deformations. The consequence is the useful part: the ratio C/B is 0.250 at the top of the bracket and at the bottom and everywhere between, because the polar second moment of a circle is exactly twice its flexural one. Mechanics and drape

Where a torsion model stops

A second stiffness was added because an earlier ladder named its absence as the first thing to disbelieve. It settled four things, refuted one trade explanation, and left the question it was built for exactly where it found it.

 Two stiffnesses, one bracket, and a ratio that does not move. The bending and torsional rigidities of a cotton yarn against its count, each drawn at both ends of its own bracket, on a logarithmic scale. The four curves are two parallel pairs: the torsional bracket is the bending bracket exactly — the fibre count over the square of the packing factor, 327 at 20 tex — so the vertical gap between the two bounds is the same for both deformations. The consequence is the useful part: the ratio C/B is 0.250 at the top of the bracket and at the bottom and everywhere between, because the polar second moment of a circle is exactly twice its flexural one. Mechanics and drape

Where this collection's thread model now stands

A thread has two stiffnesses and a thickness, and this collection's model has had one stiffness and no thickness. Both were added in one phase, neither reached the question it was built for, and the accounting is worth more than either.

The whole library · All essays