Yarn stiffness — the series · Textile Structure

The two calculations a yarn's stiffness admits. A bundle of 9 fibres bent with the fibres free to slide and with them locked together. Free, the rigidity is the sum of the fibres': 0.00141 N·mm² for a 30 tex cotton yarn. Locked, it is the fourth power of the yarn's own diameter: 0.689. The ratio is the fibre count over the square of the packing factor, 490, and nine fibres are drawn where the yarn has 176. What the drawing cannot show is where a real yarn sits between them, which is a question about friction rather than about fibre.

A yarn's stiffness is a bracket, not a number

Two calculations are available for how stiff a thread is in bending, and both are exact. One treats the fibres as free to slide and gives the sum of their stiffnesses; the other treats them as locked and gives a solid rod. They differ by the fibre count, which for an ordinary cotton yarn is a factor of five hundred — and no measurement of the fibre narrows it by anything at all.

part 1 · mechanics

What a shed costs, in newtons. The tension the shed puts into one end at each shaft of a 24-shaft harness, for a 25 tex cotton yarn. The strain is set by the loom's geometry alone; the tension is that strain times the yarn's modulus. The front shaft holds 0.52 N and the back 1.95 N, which is 14 and 52 per cent of the yarn's breaking load. What the chart cannot show is the rest of the warp tension, which the let-off adds on top of all of these and which no geometry decides.

What the shed costs, in newtons

The shed's strain has been computed here and could not be priced: a strain is a length over a length and says nothing about how hard a thread is being pulled. A modulus turns it into a tension — and the back shaft of a twenty-four-shaft harness turns out to hold its ends at half their breaking load, all day, from the geometry alone.

part 2 · mechanics

Cotton and viscose in every column this site carries. The two cellulosic fibres compared across every constant on this site. Both are cellulose at 1.52 g/cm³, both are given a modulus of 8 GPa and a fineness of 1.7 dtex, so a 20 tex yarn of either has the same diameter to the last figure — and therefore the same crimp, the same cover, the same jamming sett and the same bending bracket. Every geometric result on this site is the same number for the two fibres. Water separates them twice: viscose swells 1.75 times as far across and loses half its strength where cotton gains a tenth. What the table cannot show is why, which is a question about how cellulose is arranged inside a fibre and is not in this collection.

Water tells two fibres apart

Cotton and viscose are the same material by every constant this collection carries. Same density, same modulus, same fineness, so the same diameter at every count and the same crimp, cover, jamming sett and bending bracket. A wash separates them by a factor of two, and it is the only thing here that can.

part 3 · mechanics

Elastic recovery against strain, for seven fibres. The elastic recovery of seven fibres at the strains it is reported at: extend to a stated strain, unload, read the strain returned immediately. Each fibre's points are joined and the line stops where the measurements stop, which is the point of the figure — a fibre strained past the last point on its own line is a fibre this collection declines to answer for. Nothing here is measured below one per cent of strain, and a woven cloth just past its own interchange budget is at a thread strain of a few hundredths, so the region that matters most for a fabric is the region nobody has reported. Recovery falls monotonically for every fibre, which is what lets the unmeasured region be bracketed between the lowest measured value and one rather than extrapolated. What the plot cannot show is the delayed recovery, which is excluded by the convention and is largest for the fibre with the best reputation for recovering.

Recovery is measured and nothing predicts it

A fibre's stiffness is a bracket this collection can compute the ends of. What fraction of a strain it gives back is not: it has to be looked up, the tables are thin, they stop exactly where a fabric needs them, and the most attractive explanation for the ordering they show turns out to have no signal in it at all.

part 4 · mechanics

Which end of the bracket a thread in cloth is at. A yarn bends as a solid rod while its fibres cannot slide and as a loose bundle once they can, and the crossover is a curvature: the coherent state demands an axial force in the outer fibre that has to be built up by friction under the twist's own radial pressure. The curves are the crossover radius against twist at four contact efficiencies, the top one being 1.0 — the claim that fibres touch along their whole length, which nobody makes. The rule at the bottom is the radius a thread is bent to by its own crimp in a cloth, about 0.25 mm. Every curve is above the rule by at least 19-fold, so a thread in cloth is at the free end of its bracket at every twist and every efficiency, and the collection's habit of using the lower bound is a result rather than a convention.

Twist decides where in the bracket

A yarn's bending rigidity can only be bracketed, and the bracket is three hundred wide. What decides where a yarn sits in it is whether its fibres can slide — and for a thread bent by its own crimp in a cloth, the answer is not close.

part 5 · mechanics

Two stiffnesses, one bracket, and a ratio that does not move. The bending and torsional rigidities of a cotton yarn against its count, each drawn at both ends of its own bracket, on a logarithmic scale. The four curves are two parallel pairs: the torsional bracket is the bending bracket exactly — the fibre count over the square of the packing factor, 327 at 20 tex — so the vertical gap between the two bounds is the same for both deformations. The consequence is the useful part: the ratio C/B is 0.250 at the top of the bracket and at the bottom and everywhere between, because the polar second moment of a circle is exactly twice its flexural one.

A fabric reads its own bracket four ways

A yarn's stiffness is unknown to a factor of three hundred, and no laboratory measurement has closed it. Four unrelated everyday observations — a snarl, a knot, a flattened yarn and a cloth's own thickness — all say the same thing about which end of it a yarn sits at.

part 6 · mechanics