Textile Structure
how cloth is put together
Series

Torsion — the series

4 essays on one idea, from the one that introduces it to the one that assumes the rest.
  1. A fibre's two stiffnesses, as the ratio that survives the bracket. C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it.

    A thread has a second stiffness

    Every mechanical number here came from one material constant: how hard a thread is to bend. A thread also resists being twisted, nothing here has ever used that, and the ratio between the two turns out to be the only stiffness number about a yarn that can be known at all.

    part 1 · mechanics
  2. Twist is not torsion: a straight rod, twisted. A rod drawn with a cross painted along it, and the cross turned through 1.5 full turns from one end to the other. The rod is straight, so it has no Frenet frame at all — a straight line has no osculating plane to turn. The two discs above are the rod's ends seen down its own axis, which is where the twist is an angle rather than a foreshortened wiggle. The twist is the rotation of the painted cross about the rod's own tangent, and it is 1.5 turns whatever the centre line does. That is the quantity a torsional rigidity resists, and it is why a collection that solved a plane curve had not thereby dealt with torsion.

    Twist is not torsion

    A curve has a torsion and a material has a twist, they share a word, and only one of them is what a torsional rigidity resists. Getting them the wrong way round would have made this collection conclude that a knitted loop carries no twist, on the strength of a theorem that says nothing of the kind.

    part 2 · mechanics
  3. A fibre's two stiffnesses, as the ratio that survives the bracket. C over B for every fibre in the table, at 20 tex, which is 2G/E and nothing else. The mark beyond each bar is the range the shear modulus is reported over. Glass is the control and is not a measurement: it is a drawn isotropic solid, so its ratio must be 1/(1+ν) and at ν = 0.2 that is 0.833, which is what the table says. Every fibre with molecules drawn out along its axis sits below the isotropic value, and the ordering is the subject rather than an accident — a fibre is stiff along its axis because its molecules are drawn out along it, and the same orientation that raises E leaves G to whatever holds one chain to the next. Aramid, the most oriented thing here, is twenty times softer in torsion relative to its bending than the glass beside it.

    The one fibre whose answer is known

    A table of measured constants is worth what its worst row is worth, and nobody can tell which row that is. This one has a member whose answer was known before anybody measured it, and the ordering of the other nine turns out to say something about how fibres are made.

    part 3 · mechanics
  4. Two stiffnesses, one bracket, and a ratio that does not move. The bending and torsional rigidities of a cotton yarn against its count, each drawn at both ends of its own bracket, on a logarithmic scale. The four curves are two parallel pairs: the torsional bracket is the bending bracket exactly — the fibre count over the square of the packing factor, 327 at 20 tex — so the vertical gap between the two bounds is the same for both deformations. The consequence is the useful part: the ratio C/B is 0.250 at the top of the bracket and at the bottom and everywhere between, because the polar second moment of a circle is exactly twice its flexural one.

    Where a torsion model stops

    A second stiffness was added because an earlier ladder named its absence as the first thing to disbelieve. It settled four things, refuted one trade explanation, and left the question it was built for exactly where it found it.

    part 4 · mechanics

All series