Z twist at 800 turns per metre

A 20 tex cotton yarn, 0.167 mm across, with its surface fibres drawn as the helices they are. The angle between a surface fibre and the yarn's axis is 22.8°, and it is the only quantity in this family: the yarn is 4.1% shorter than the fibre in it and carries 85% of the strength the same fibre would give lying straight.

3 essays call twist. The drawing above is what it returns with no arguments at all; every call below passes it something, because a placement that passes nothing draws whichever member of the family the generator happens to default to rather than the weave its essay argues about.

Where it is called

Changing this generator changes every one of these figures.

Z twist at 800 turns per metre. A 20 tex cotton yarn, 0.167 mm across, with its surface fibres drawn as the helices they are. The angle between a surface fibre and the yarn's axis is 22.8°, and it is the only quantity in this family: the yarn is 4.1% shorter than the fibre in it and carries 85% of the strength the same fibre would give lying straight.

Setting and geometry

Twist is one angle

Every model on this site treats a yarn as a cylinder with a diameter. It is a bundle of loose fibres, and what makes it behave like a cylinder is twist — which is a helix, so the whole subject is one angle, and the trade's twist factor turns out to be the only combination of count and turns that decides anything.

Z twist at 1600 turns per metre. A 20 tex cotton yarn, 0.167 mm across, with its surface fibres drawn as the helices they are. The angle between a surface fibre and the yarn's axis is 40.0°, and it is the only quantity in this family: the yarn is 13.8% shorter than the fibre in it and carries 59% of the strength the same fibre would give lying straight.

Weaves

The other crepe is in the yarn

A crepe weave puts the texture in the matrix. A crepe yarn puts it nowhere the matrix can see: the cloth is a plain weave, and the surface comes from a thread twisted so hard that it shortens by a seventh and spends the rest of its life trying to untwist.

Both halves of the twist curve, at 28 mm staple. The falling curve is obliquity and is exact — the affine end of the bracket, computed from the helix and nothing else. The rising curve is cohesion and is the half this collection had declined: a fibre end is gripped by friction under the twist's own radial pressure, the fibre's strength and the yarn's load cancel out of the comparison, and what is left is a critical length that depends on the twist through a pure function of the angle. Their product has a maximum at a twist factor of 3101 — 693 turns per metre at 20 tex, a surface angle of 20° — which is inside the range spinners use. The scale of the rising curve is fitted, through a contact efficiency of 0.05, and moving it moves the optimum; what it cannot move is the ordering between two staples or two fibres, which is what the two claims made from this figure are about.

Setting and geometry

The other half of the twist curve

This collection computed the falling half of the strength–twist curve exactly and declined the rising half as being out of reach. It is not out of reach. With the grip derived rather than assumed, the optimum comes out at a twist factor — and the same twist factor at every count, which is why the trade quotes twist factors at all.