A coating over the hole it has to bridge

A coating over the hole it has to bridge
A coating over the hole it has to bridge. Four warp ends of 40 tex seen end-on at 20 per centimetre, with a 120 micrometre PVC film over them. The film is supported everywhere it lies on a thread and unsupported over the 252 micrometre clear span between them, which is the same span at every hole in the repeat. The film's thickness is drawn to scale against that span; the bulge is exaggerated. At 20 MPa the film will hold at most 381 bar, which is a bound and not a prediction.

Four warp ends of 40 tex seen end-on at 20 per centimetre, with a 120 micrometre PVC film over them. The film is supported everywhere it lies on a thread and unsupported over the 252 micrometre clear span between them, which is the same span at every hole in the repeat. The film's thickness is drawn to scale against that span; the bulge is exaggerated. At 20 MPa the film will hold at most 381 bar, which is a bound and not a prediction.

2 essays call coat-section. The drawing above is what it returns with no arguments at all; every call below passes it something, because a placement that passes nothing draws whichever member of the family the generator happens to default to rather than the weave its essay argues about.

Where it is called

Changing this generator changes every one of these figures.

What a coating does to the rest of the site. Seven quantities this site computes for uncoated fabric, with what each becomes once a film bonds the crossings: the shear a cloth will take — changed in kind; tear strength — changed in kind; the loss from a hole — reversed; wicking — halved; air permeability — reversed; the sett's effect on strength — unchanged in sign; areal weight — added to. Two of the seven reverse outright. The table is a collection rather than a computation, and each row points at the essay whose result it qualifies. After the loom

Coated is a state

Every mechanism on this site assumes threads that can move relative to one another — the bias is a mechanism because the crossings rotate, a tear runs because threads gather, a cloth takes a hole without minding because the neighbours pick the load up. A film bonds the crossings. Two of those results reverse outright, the rest change in kind, and no number on this site has ever said which state it belongs to.

 A coating over the hole it has to bridge. Four warp ends of 40 tex seen end-on at 20 per centimetre, with a 120 micrometre PVC film over them. The film is supported everywhere it lies on a thread and unsupported over the 252 micrometre clear span between them, which is the same span at every hole in the repeat. The film's thickness is drawn to scale against that span; the bulge is exaggerated. At 20 MPa the film will hold at most 381 bar, which is a bound and not a prediction. Cloth doing a job

A coated cloth fails at its holes

Spread a film over a fabric and it is supported everywhere it lies on a thread and unsupported over every hole. A woven cloth's holes are all the same size — exactly, because a repeat is a repeat — so the film has one span to bridge and the fabric has a burst pressure rather than a distribution. A nonwoven gives it a distribution, and a membrane fails at the largest hole it meets.